多层薄膜结构气敏效应研究

在SnO2气敏薄膜层上覆盖一层或多层钝化材料（SiO2,Al2O3) 薄膜，制成的多层膜气敏元件，可很好地排除大分子气体如乙醇等对小分子H2检测的干扰，使其具有单独检测H2的功能。本文还通过测量元件的升温曲线，推导出敏感体表面的氧吸附活化能；找出活化能与灵敏度、选择性的关系。根据实验现象和物性分析结果，试着探讨了元件的敏感机理。     

用菱锌矿制取轻质氧化锌的研究

介绍了以菱锌矿为原料生产轻质氧化锌的方法，论述了反应酸浓度，煅烧温度，溶液PH值对实验的影响，并对生产工艺条件进行了研究。其工艺流程是将粉碎后的菱锌矿进行循环酸浸，净化后再直接和碳化母液反应，经沉降后再煅烧分解为轻质氧化锌，产品质量符合国家标准，视比容大，活性强，成本低，经济效益显著。     

Preparation, Characterisation and Catalytic Behaviour of a New TeVMoO Crystalline Phase

TeM_xMo_1.7O mixed oxides (M = V and/or Nb; x = 0-1.7) have been prepared by calcination of the corresponding salts at 600 °C in an atmosphere of N₂. A new crystalline phase, with a Te/V/Mo atomic ratio of 1/0.2-1.5/1.7, has been isolated and characterised by XRD and IR spectroscopy. This phase is observed in the TeVMo or TeVNbMo mixed oxide but not in the TeNbMo mixed oxide. The new crystalline phase shows an XRD pattern similar to Sb₄Mo₁₀O₃₁ and probably corresponds to the M1 phase recently proposed by Aouine et al. (Chem. Commun. 1180, 2001) to be present in the active and selective MoVTeNbO catalysts. Although these catalysts present a very low activity in the propane oxidation, they are active and selective in the oxidation of propene to acrolein and/or acrylic acid. However, the product distribution depends on the catalyst composition. Acrolein or acrylic acid can be selectively obtained from propene on Nb-free or Nb-containing TeVMo catalysts, respectively. The presence of both V and Nb, in addition to Mo and Te, appears to be important in the formation of acrylic acid from propene.     

The Synthesis of Sulfated Titanium Oxide Nanotubes

TiO₂ nanotubes can be prepared in gram quantities by treating anatase TiO₂ powder with concentrated NaOH solution. These TiO₂ nanotubes acquired strong acidity after being impregnated with sulfuric acid solution and calcined at 300 °C. The anatase TiO₂ powder used to prepare the nanotube did not catalyze the esterification between cyclohexanol and acetic acid, while sulfated TiO₂ nanotubes were very reactive toward the esterification reaction.     

Growth Stresses in the Oxide Scales on TiAl Alloys at 800 and 900°C

In the oxidation of TiAl alloys, the role of scale-growth stresses formed during oxidation has, thus far, been unknown. In the present paper the oxide-growth stresses were investigated by the deflection-test method in monofacial oxidation (DTMO) accompanied by acoustic-emission measurements. On unmodified surfaces the growth stresses are compressive and reach levels of around –100 MPa. At the same time, significant acoustic emission occurs indicating that even under isothermal conditions, stresses are relieved by a scale-cracking mechanism. For oxide scales on TiAl surfaces, which had been ion implanted with chlorine before oxidation, a very thin protective alumina layer is formed which, however, develops growth stresses in the range of several GPa, accompanied by intensive acoustic emission. In all stress–time curves, a dynamic situation is observed. This consists of phases of stress relief by scale microcracking and phases of stresses increase due to crack healing and further oxide growth. As a result, the level of stress as a function of oxidation time, is characterized by an oscillating course.     

Immobilization and activation of vanadium(III) and titanium(III) single‐site catalysts for ethylene polymerization using MgCl2‐based supports

Significant increases in the activity of vanadium(III) amidinate catalysts for ethylene polymerization have been obtained by immobilization on a MgCl₂‐based support prepared by reaction of AlEt₃ with a MgCl₂/ethanol adduct. Catalyst immobilization and activation on this type of support prevents the rapid decay in activity observed under homogeneous polymerization conditions with unsupported catalysts. Stable polymerization activity is also observed with analogous titanium(III) complexes. Polyethylene with narrow molecular weight distribution and spherical particle morphology is obtained without reactor fouling. Copyright © 2005 Society of Chemical Industry     

掺杂VO2的特性、制备方法及应用

VO2在68℃时发生从低温的单斜相向高温四方相转变，同时伴随着光、电、磁性能的突变。通过掺入其它杂质元素，能有效改变其相变温度和光、电性能，这些优异特性使其具有更好的应用前案。本文综述了掺杂的原理，掺杂对VO2相变影响、常用的掺杂方法及目前的应用情况，这对其进一步的研发应用具有重要的意义。     

熔融碳酸盐燃料电池阴极材料的导电性

通过交流阻抗方法研究了熔融碳酸盐燃料电池阴极材料锂镍氧化物、锂钴氧化物和锂铁氧化物的导电性能。结果表明:锂镍氧化物电极的导电性最好,锂钴氧化物电极的导电性次之,锂铁氧化物电极的导电性最差;它们的导电性都随着温度的升高而按指数规律增加;在合成锂钴氧化物(或锂铁氧化物)的过程中,使Li2CO3轻微过量,可以提高锂钴氧化物(或锂铁氧化物)电极的导电性,而且在同一温度下,随着nLi∶nCo(或nLi∶nFe,摩尔比)值的增大,锂钴氧化物(或锂铁氧化物)电极的导电性显著增加。     

Relating catalyst structure and composition to the water–gas shift activity of Cu–Zn-based mixed-oxide catalysts

In order to investigate the effect of cerium oxide on Cu–Zn-based mixed-oxide catalysts four catalyst samples were characterized by means of XRD, in situ XANES and thermogravimetric analysis. The activity of the catalyst samples was tested for the forward water–gas shift reaction. Cerium oxide was found to increase the crystallinity of the ZnO phase indicating a segregation of the Cu and ZnO phases. The TOF of the water–gas shift reaction based on chemisorption data was found to be independent of composition and preparation conditions of the four catalyst samples. In contrast, the catalyst stability depends on composition and preparation conditions. Cerium oxide impregnated before calcination of the hydrotalcite-based Cu–Zn precursors leads to a more stable water–gas shift catalyst.     

介孔氧化铁对正辛醇乙氧基化反应的催化性能

以十二烷基磺酸钠为模板剂、乙二胺为碱性介质,将水热法合成的氧化铁/十二烷基磺酸钠复合中孔材料在550℃、空气气氛中煅烧10h,除去模板剂,得到介孔氧化铁。通过X射线衍射、氮气吸附-脱附方法对介孔氧化铁的晶体结构和表面物性进行表征。表征结果显示,煅烧后的介孔氧化铁具有典型的六方介孔的结构特征,平均孔径为5.4nm。将介孔氧化铁用于催化正辛醇乙氧基化反应,研究结果表明,升高反应温度和初始压力、增加催化剂用量,可加快环氧乙烷的反应速率,同时产物的相对分子质量分布较窄。当平均聚合度为6.5时,正辛醇聚氧乙烯醚相对分子质量分布的选择性系数达到21.1。